MIL-PRF-19500/565E
4.3.1 Gate stress test. Apply VGS = -30 V minimum for t = 250 µs minimum.
4.3.2 Unclamped inductive switching.
a.
Peak current (ID)
2N6895
1A
2N6896
2.7 A
2N6897
5A
2N6898
5.9 A
b.
Peak gate voltage (VGS) ............................................. 10 V.
Gate to source resistor (RGS) .................................... 25Ω ≤ RGS ≤ 200Ω.
c.
Initial case temperature (TC) ...................................... +25°C, +10°C, -5°C.
d.
Inductance (L).............................................................. 100 μH ±10 percent.
e.
f.
Number of pulses to be applied................................... 1 pulse minimum.
g.
Pulse repetition rate..................................................... None.
* 4.3.3 Thermal impedance. The thermal impedance measurements shall be performed in accordance with method
3161 of MIL-STD-750 using the guidelines in that method for determining IM, IH, tH, tSW, (and VH where appropriate).
Measurement delay time (tMD) = 70 μs max. See table II, group E, subgroup 4 herein.
4.3.4 Power burn-in. Power burn-in conditions are as follows: Method 1042 of MIL-STD-750, condition C,
TA = +25°C, -5°C, +10°C, VDS = 10 V min.; ID adjusted to meet a junction temperature of +140°C, - 5°C, + 10°C, t =
240 hours.
4.4 Conformance inspection. Conformance inspection shall be in accordance with MIL-PRF-19500. Alternate
flow is allowed for conformance inspection in accordance with figure 4 of MIL-PRF-19500.
4.4.1 Group A inspection. Group A inspection shall be conducted in accordance with MIL-PRF-19500 and table I
herein. Electrical measurements (end-points) shall be in accordance with the inspections of table I, subgroup 2
herein.
8